52H Glass Sealing52 Vacodil 520 Wire 0.5mm and 0.8mm large in stock with fast delivery
|
Szczegóły Produktu:
Zapłata:
|
Szczegółowy opis produktu
| Materiał: | Stop 52 | Rodzaj materiału: | Precyzyjny stop |
|---|---|---|---|
| Średnica: | 0,05 mm ~ 10 mm | Pakiet: | Szpula i cewka |
| Waga cewki: | 5 ~ 50 kg | Nazwa zwyczajowa: | FeNi52 |
| Podanie: | Szklana metalowa uszczelka | Chemia: | Fe, Ni Alloy |
| Rodzaj stopu: | Expansion Alloy | ||
| Podkreślić: | 52H Szklany drut uszczelniający,0.8mm Szklany drut uszczelniający,0.5mm Szklany drut uszczelniający |
||
52H Glass Sealing52 Vacodil 520 Wire 0.5mm and 0.8mm large in stock with fast delivery
Product Description
The iron-nickel fixed expansion alloy is a series of fixed expansion alloys that can be matched with soft glass and ceramics with different expansion coefficients in a given temperature range by adjusting the nickel content. The expansion coefficient and Curie point increase with the increase of nickel content. This combination gold is a widely used sealing structure material in the electric vacuum industry
Chemical Composition
| Grade | C% | P% | S% | Mn% | Si% | Cu% | Cr% | Mo% | Ni% | Co% | Fe% |
| Alloy52 | Max 0.05 | Max 0.020 | Max 0.020 | Max 0.80 | Max 0.30 | / | / | / | 51.5~52.5 | / | Bal. |
Specifications
| Grade | Common Name | Common Name |
| Alloy52 | Vacodil520 | NILO 52 |
Physical Properties
| Grade | Density | Resistivity |
| Alloy52 | 8.25 g/cm3 | 0.43 |
Grain size of Alloy52
The grain size of the alloy deep-drawing belt should not be less than level 7, and the grain size less than level 7 should not exceed 10% of the area. When the average grain size of the strip with a thickness of less than 0.13mm is estimated, the number of grains along the thickness of the strip should be no less than 8.
Welding performance of Alloy52
The combined gold has good welding performance and can be brazed and spot welded. The combination of gold and soft glass should be pre-oxidized before sealing.
Coefficient of Expansion
| Alloy | Linear Coefficient of Thermal Expansion a,10-6/°C | |||||||
| 20-200°C | 20-300°C | 20-350°C | 20-450°C | 20-500°C | 20-600°C | 20-700°C | 20-800°C | |
| Kovar | 10.4 | 10.2 | 10.3 | 10.3 | 10.3 | 10.8 | / | / |
Heat Treatment For Alloy52
(1) Stress relief annealing In order to eliminate the residual stress of parts after machining, stress relief annealing is required: 430~540℃, heat preservation 1~2h, furnace cooling or air cooling. [1]
(2) Intermediate annealing In order to eliminate the work hardening phenomenon caused by the alloy in the process of cold rolling, cold drawing and cold stamping, in order to facilitate the continued processing. The workpiece needs to be heated to 700~800℃ in a vacuum or protective atmosphere for 30~60min, then furnace cooled, air cooled or water quenched.
(3) Pre-oxidation treatment When the combined gold is used as a sealing material, it should be pre-oxidized before sealing. A uniform and dense oxide film is formed on the surface of the alloy. The parts are heated in saturated wet hydrogen at 1100°C for 30 minutes, and then oxidized in the air at about 800°C for 5-10 minutes. The weight gain of the parts should be 0.1~0.3mg/cm2
Company Profile
Customer Photos
Exhibition
Production Process
Testing Equirement
Shipment
Contact Us
Szczegóły kontaktu
Ohmalloy Material Co.,Ltd
Osoba kontaktowa: Jully
Tel: +8617301602658
Wyślij zapytanie bezpośrednio do nas
Jeszcze Precyzyjne stopy
-
Precyzyjny stały stop magnetyczny 3J53 podobny do rozpiętości Ni C.
-
Rury kapilarne Invar36 FeNi36 precyzyjne, stosowane w przemyśle medycznym
-
Najwyższej jakości gotowa zaprawa tuby Kovar / rury 4J29 / 29HK
-
Drut ze stopu niklowanego Fe NiCo17 do uszczelniania i dopasowywania materiałów ceramicznych
-
Stopy niklowe do odkurzania do szklanych - do - metalowych uszczelek do rur próżniowych
-
Włókno z termoparą z rodu platynowego typu S/R/B do wykrywania temperatury